Fluoride release and recharge behavior of a nano-filled resin-modified glass ionomer compared with that of other fluoride releasing materials.

Abstract

The cumulative amount of fluoride released from KN, VT and FLC and the release profiles were statistically similar but greater than that for FIX at P < 0.05. All four materials, including KN, showed a burst of fluoride ions at shorter times (t) and an overall rate dependence on t1/2 typical for glass-ionomers. The coating of KN with its primer and of DY with its adhesive did not significantly alter the fluoride release behavior of the respective materials. The overall rate for KN was significantly higher than for the compomer DY. DY showed a linear rate of release vs. t and no burst effect as expected for compomers. The nanoionomer KN showed fluoride recharge behavior similar to the conventional glass ionomers FIX and KM. Thus, it was concluded that the new RMGI KN exhibits fluoride ion release behavior similar to typical conventional and RMGIs and that the primer does not impede the release of fluoride.