Experiences on corrosion inhibitors for reinforced concrete

Abstract

Corrosion of carbon steel reinforcement is the most important cause of premature failure on reinforced concrete structures. Prevention of corrosion is primarily achieved in the design phase by using high quality concrete and adequate cover. Additional prevention methods are adopted when severe environmental conditions occur or on structures\nrequiring very long service life. Among these methods, corrosion inhibitors seem to offer a simple and cost effective prevention technique. They may be used both as a preventative techniques, if added to fresh concrete, and as a repair system, if applied on hardened concrete.\nThe performance of corrosion inhibitors for reinforced concrete structures affected by chloride induced and carbonation corrosion has been studied at PoliLaPP, Laboratory of Corrosion of materials "P. Pedeferri" of the Department of Chemistry, Materials and\nChemical Engineering "G. Natta", Politecnico di Milano, in the last 15 years.\nOrganic commercial admixed corrosion inhibitors delayed the occurrence of chloride induced corrosion. This result is related to two effects: reduction of the rate of chloride transport into concrete and increase of the critical chloride threshold.\nCommercial migrating corrosion inhibitors (MCI) are able to delay time-to-corrosion of passive rebars in concrete subjected to chlorides ponding; this effect is mainly related to the reduction of chlorides diffusion coefficient. MCI can reduce the corrosion rate after\ncorrosion initiation only in carbonated concrete, nevertheless efficiency is low and residual corrosion rate is not negligible.\nCommercial MCI can penetrate into concrete mainly through capillary sorption but penetration depth is limited to 20 mm.\nThe results obtained with nitrite-based inhibitor confirm literature data: the inhibitor is effective if the molar ratio [NO2 ]/[Cl ] is higher than 0.5-0.6; in carbonated concrete, due to insufficient amount of inhibitor, no significant effect has been observed on corrosion rate.\nAmong the tested organic substances, compounds containing carboxylic group showed the best results solution tests: pitting potential, time-to-corrosion and critical chloride content are similar to those obtained with sodium nitrite. In concrete tests, only one amine and one amino acid showed good performance increasing the critical chlorides threshold with respect to the reference condition. For carboxylate substances, a strong link was found between inhibiting properties and molecular structure.