<i>n</i>-Type Bi₂Te_3–<i>x</i>Se_<i>x</i> Nanoplates with Enhanced Thermoelectric Efficiency Driven by Wide-Frequency Phonon Scatterings and Synergistic Carrier Scatterings

Abstract

Driven by the prospective applications of thermoelectric materials, massive efforts have been dedicated to enhancing the conversion efficiency. The latter is governed by the figure of merit (ZT), which is proportional to the power factor (S(2)σ) and inversely proportional to the thermal conductivity (κ). Here, we demonstrate the synthesis of high-quality ternary Bi2Te3-xSex nanoplates using a microwave-assisted surfactant-free solvothermal method. The obtained n-type Bi2Te2.7Se0.3 nanostructures exhibit a high ZT of 1.23 at 480 K measured from the corresponding sintered pellets, in which a remarkably low κ and a shift of peak S(2)σ to high temperature are observed. By detailed electron microscopy investigations, coupled with theoretical analysis on phonon transports, we propose that the achieved κ reduction is attributed to the strong wide-frequency phonon scatterings. The shifting of peak S(2)σ to high temperature is due to the weakened temperature dependent transport properties governed by the synergistic carrier scatterings and the suppressed bipolar effects by enlarging the band gap.