Functionalization of Cotton Fiber by Partial Etherification and Self-Assembly of Polyoxometalate Encapsulated in Cu₃(BTC)₂ Metal–Organic Framework

Abstract

A combination of a Keggin-type polyoxometalate (POM), [CuPW11O39](5-), with a Cu3(BTC)2 metal-organic framework (MOF-199/HKUST-1; where BTC is benzene-1,3,5-tricarboxylate), was successfully self-assembled on a cellulose substrate (cotton) with a room-temperature process. Cotton fibers were functionalized by partial etherification. Cu3(BTC)2 metal-organic framework and polyoxometalate encapsulated in Cu3(BTC)2 metal-organic framework were self-assembled on the carboxymethylate ion sites initiated with copper nitrate using ethanol and water as solvents. Octahedral crystals were observed on both MOF-cotton and POM-MOF-cotton; both contained copper while the POM-MOF-cotton also contained tungsten. Occupancy of POM in MOF cages was calculated to be about 13%. Moisture content remained at 3 to 4 wt % similar to that of untreated cotton. Reactivity to both hydrogen sulfide and methyl parathion was higher for POM-MOF-cotton due to the Keggin polyoxometalate and the extra-framework cations Cu(2+) ions compensating the charges of the encapsulated Keggins. The POM-MOF material was found to effectively remove 0.089 mg of methyl parathion per mg of MOF from a hexane solution while MOF-cotton removed only 0.054 mg of methyl parathion per mg of MOF.