Thermal stability, flame retardance, and mechanical properties of polyamide 66 modified by a nitrogen–phosphorous reacting flame retardant

Abstract

ABSTRACT Flame‐retardant polyamide 66 (PA66) was prepared by the polymerization between PA66 prepolymer and N ‐benzoic acid (ethyl‐ N ‐benzoic acid formamide) phosphamide (NENP). Compared with the pure PA66, the flame‐retardant PA66 exhibited better thermal stability, as indicated by thermogravimetric analysis results. The limiting oxygen index was 28% and the UL‐94 test results of the flame‐retardant PA66 indicated a V‐0 rating when the content of the NENP prepolymer was 5 wt %. The flammability and flame‐retardant mechanism of PA66 were also studied with cone calorimetry and scanning electron microscopy/energy‐dispersive X‐ray spectroscopy, respectively. The mechanical properties results show that the flame‐retardant PA66 resin had favorable mechanical properties. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 133 , 43538.