The structural, micro structural and electric properties have been investigated for lead oxide doped strontium titanate ceramics synthesized via conventional solid state diffusion method which were calcined at 900 0 C for 13hr and sintered at 1000 0 C for 4hrs respectively. The strong relaxation dynamics in loss factor was observed at higher temperatures. AC- conductivity variations with temperatures were studied and the activation energies (Ea) were calculated of the range 0.24-0.94eV using the lnσ Vs 1/T plots. The crystalline sizes were found to be varying from 77nm-109nm by means of XRD and the FTIR spectrum was recorded over a continuous spectral range of 400-4000cm -1 to