A magnetic recording tape based on iron particles

Abstract

Tapes based on acicular iron particles give an outstanding recording performance compared to γ-Fe <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> O <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> and CrO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> tapes. Especially in the short wavelength region the signal to noise ratio is, respectively, 12 and 7 dB better, whereas the bias noise level is somewhat lower. The iron tapes have a high coercivity, between 80 and <tex xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">90 \times 10^{3}</tex> A/m, and hence the required bias is about 9 dB higher than for γ-Fe <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> O <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> . The print through properties are excellent.