Effect of hygrothermal ageing on the monotonic and cyclic loading of glass fiber reinforced polyamide

Abstract

The properties of short glass fiber reinforced thermoplastic based on polyamide 6 in humid environment are studied. Conditioning was conducted at 90°C. The combined action of water and heat (90°C) affects progressively the mechanical properties. When the injection molded samples were subjected to moisture, decrease in tensile strength and elastic modulus was observed whatever in distilled water or in salt solution. However, there is an enhancement of elongation at break with increasing exposure to humidity. After immersion in water, the fatigue life time is drastically reduced. Scanning electron microscope (SEM) was used in order to examine the fractured samples feature. Results show that water diffuses into the polymer leading to a reduction of the interfacial stress transmissibility. The major contributor of the stiffness loss is the adhesion loss between the fibers and the polymer. POLYM. COMPOS., 35:501–508, 2014. © 2013 Society of Plastics Engineers