Effect of Additional Elements on the Structural Properties, Magnetic Characteristics and Natural Resonance Frequency of Strontium Ferrite Nanoparticles/Polymer Composite

Abstract

Substituted strontium ferrites SrFe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">12-x</sub> Mg <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">x/2</sub> Sn <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">x/2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">19</sub> (x=1 , 2 and 3) were prepared by sol-gel method. X-ray diffraction (XRD), transmission electron microscope (TEM), AC susceptometer, vibrating sample magnetometer (VSM) and vector network analyzer were used to analyze the structure, static and dynamic magnetic properties of the prepared samples. The prepared ferrite particles possess irregular non spherical shape with a broad size distribution. The substitution was very effective in reducing coercive field. Based on microwave measurements of reflectivity, SrFe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">12-x</sub> Mg <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">x/2</sub> Sn <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">x/2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">19</sub> is a good candidate for electromagnetic compatibility and other practical applications at high frequencies.