Synthesis and Properties of a Water‐Soluble Single‐Walled Carbon Nanotube–Poly(<i>m</i>‐aminobenzene sulfonic acid) Graft Copolymer

Abstract

Abstract Poly( m ‐aminobenzene sulfonic acid) (PABS), was covalently bonded to single‐walled carbon nanotubes (SWNTs) to form a water‐soluble nanotube–polymer compound (SWNT–PABS). The conductivity of the SWNT–PABS graft copolymer was about 5.6 × 10 –3 S cm –1 , which is much higher than that of neat PABS (5.4 × 10 –7 S cm –1 ). The mid‐IR spectrum confirmed the formation of an amide bond between the SWNTs and PABS. The 1 H NMR spectrum of SWNT–PABS showed the absence of free PABS, while the UV/VIS/NIR spectrum of SWNT–PABS showed the presence of the interband transitions of the semiconducting SWNTs and an absorption at 17 750 cm –1 due to the PABS addend.