Retrograde Densification in Bi ₂ Sr ₂ CaCu ₂ O ₈ Superconductors

Abstract

Bi 2 Sr 2 CaCu 2 O 8 was prepared using the mixed oxide‐carbonate method and sintered at temperatures ranging from 850° to 911°C. The samples were characterized for density, mechanical strength, phase composition, microstructure, and superconducting transition temperatures. A unique retrograde densification characteristic is demonstrated in the temperature range 850° to 890°C whereby the material first becomes less dense as the sintering temperature is raised, and only in a narrow temperature range from 900° to 905°C does the material densify then with the formation of a liquid phase. The retrograde densification mechanism is shown to be that of the formation of thin platelike crystallites which grow in a randomly oriented fashion, thus pushing the structure apart. This retrograde densification, coupled with a narrow sintering range overlapping the melting temperature, makes this compound a difficult one to process.