Fatigue & Fracture of Engineering Materials & Structures · 1983 · 70 citations · 15 references
EngineeringMaterials EngineeringMaterials ScienceMechanical Behavior Of MaterialsMetallurgyStructural MaterialsDamage MechanicsFatigueFracture MechanicsFracture PropagationFracture ToughnessStrengthening MechanismsCrack GrowthCrack Growth KineticsCrack Growth RateCrackingCracksFatigue Crack GrowthGrain BoundariesMicrocrack Growth
Abstract— The growth of “large” and “small” cracks in 7075–T6 aluminum is characterized in moist air and dry nitrogen. It is found that in both environments, the small cracks grow faster than large ones, but unlike large cracks, which grow much faster in air than in nitrogen, the small cracks extend in each environment at about the same average rate. The absence of environmental effect is found to be only apparent, a change to an inherently slower mode of growth in air offsetting the crack‐accelerating influence of moisture. Subsurface grain boundaries apparently retard microcrack growth in both environments. Possible rationales for the rapid growth of small cracks are discussed.
15