Development of Ultrafine Indium Tin Oxide (ITO) Nanoparticle for Ink-Jet Printing by Low-Temperature Synthetic Method

Abstract

<para xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink"> In this paper, an ultrafine indium tin oxide (ITO) nanoparticle for ink-jet printing was successfully developed by applying low-temperature synthetic method at 300 °C. Mean size of the synthesized ITO nanoparticle is 5 nm with uniformity. High specific surface area above <formula formulatype="inline"> <tex>$\hbox{100 m}^{2}\hbox{/g}$</tex></formula> certifies the ultrafine particle size. Especially, the ITO nanoparticle was well dispersed by the surface additive. Despite the low-temperature synthesis at 300 °C, the ITO nanoparticle was well crystallized with (2 2 2) preferred orientation. Composition ratio of In and Sn is 90 and 10 wt% in the lattice of the ITO nanoparticle. Also, using the well-dispersed ultrafine ITO nanoparticle, ITO ink was attempted to be used for ink-jet printing. As a result, ITO ink was made well by dispersing the ITO nanoparticle into the organic solvent uniformly. Using the nano-ITO ink, ITO transparent thin film with high optical transmittance over 90% could be fabricated. </para>