IEEE Transactions on Applied Superconductivity · 1999 · 10 citations · 11 references
Natural SciencesMaterials SciencePhysicsElectromagneticsElectromagnetismElectronic MaterialsMetalsSuperconducting Thin FilmsAc LossesAc Losses In WindingsFilament MaterialsFilamentary StructureSuperconducting PropertiesSuperconducting TapesSuperconducting WiresWire Material Properties
Samples of multifilamentary Bi-2223/Ag/alloy twisted filament tapes and Z stack round wires, consisting of untwisted and twisted stacks (or z-arrays) of flat filaments have been prepared. It was found that twist pitches of less than 10 mm may be incorporated into multifilament tapes while maintaining the Jc at 20 kA/cm/sup 2/. The self-field AC loss has been investigated at low frequencies up to 100 Hz. The round wire was found to exhibit isotropic electromagnetic properties.