Compatibility and viscoelastic properties of brominated isobutylene‐<i>co</i>‐<i>p</i>‐methylstyrene rubber/tackifier blends

Abstract

Abstract Brominated isobutylene‐ co‐p ‐methylstyrene (BIMS) rubber has been blended with hydrocarbon resin tackifier and alkyl phenol formaldehyde resin tackifier, and the compatibility between the blend components has been systematically evaluated. Dynamic mechanical analysis (DMA) and differential scanning calorimetry (DSC) studies show that BIMS rubber and hydrocarbon resin tackifier blends are compatible at all blend proportions studied. However, BIMS rubber and phenol formaldehyde resin blends exhibit very limited compatibility with each other and phase separation even at very low phenolic tackifier concentration. Morphological studies of the rubber–resin blends by scanning electron microscopy (SEM) corroborate well with the DMA and DSC results. From the DMA frequency sweep and temperature sweep studies, it is shown that the hydrocarbon resin tackifier acts as a diluent and causes a decrease in the storage modulus values (by reducing the entanglement and network density) in the rubbery plateau region. On the other hand, phenol formaldehyde resin behaves in the way similar to that of the reinforcing filler by increasing the storage modulus values (by increasing the entanglement and network density) in the rubbery plateau zone. The relaxation time estimated from the different zones of frequency sweep master curves provides information about the influence of the two tackifiers on the viscoelastic properties of the BIMS rubber in the respective zones. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008