The Triangular Voltage Sweep Method for Determining Double‐Layer Capacity of Porous Electrodes: IV . Porous Carbon in Potassium Hydroxide
53
Citations
0
References
1975
Year
EngineeringElectrode-electrolyte InterfaceAvailable CarbonsChemistryPotassium HydroxideChemical EngineeringCarbon-based MaterialElectrochemical InterfaceElectrode Reaction MechanismMaterials ScienceCarbon SequestrationBattery Electrode MaterialsPorous ElectrodesElectrochemical ProcessPartial WettingElectrochemistryCarbonizationPorous CarbonCarbon BlackActivated CarbonCarbon Blacks
Triangular sweep voltammetry data for a number of commercially available carbons in 31 weight per cent are discussed. A capacity minimum of 10 μf/cm2 was observed about 0V vs. for five carbon blacks. Results indicated that the carbon blacks with internal structure were completely wetted; results with one activated carbon having fine micropores (<25Å) indicated partial wetting. Experimental methods for minimizing faradaic current and distributed capacity effects are discussed.