Thermal Expansion of Rb4LiH3(SO4)4 and K4LiH3(SO4)4 Crystals in the Temperature Range from 80 to 300 K

Abstract

Thermal expansion of Rb4LiH3(SO4)4 and K4LiH3(SO4)4 crystals is studied in the temperatures ranging from 80 to 300 K. At room temperature both these crystals are isomorphic. In Rb4LiH3(SO4)4 a ferroelastic phase transition is confirmed to occur at TC = 131.2 K. In the vicinity of TC anomalous temperature changes of the thermal expansion coefficients α1, α2, and α3 as well as the components of the strain tensor (e1 + e2) and e3 are found. No anomalous changes of K4LiH3(SO4)4 thermal expansion are observed in the temperature range studied. The results of K4LiH3(SO4)4 thermal expansion investigations suggest that anomalous changes in spontaneous polarization of this crystal, observed in pyroelectric studies at about 114 K, seem to be not a consequence of structural changes in the lattice parameters of this crystal. Es wird die thermische Ausdehnung von Rb4LiH3(SO4)4- und K4LiH3(SO44-Einkristallen in Temperaturbereich von 80 bis 300 K untersucht. Bei Zimmertemperatur sind die beiden Kristalle isomorph. In Rb4LiH3(SO4)4 wird der Übergang zur ferroelastischen Phase bei der Temperatur TC = 131,2 K bestätigt. In der Umgebung von TC werden sowohl anomale Temperaturänderungen der thermischen Ausdehnungskoeffizienten α1, α2 und α3 als auch der Komponenten des Formänderungstensors (e1 + e2) und e3 festgestellt. Es werden keine anomalen Änderungen der thermischen Ausdehnung von K4LiH3(SO4)4 im untersuchenden Temperaturbereich beobachtet. Die Ergebnisse der thermischen Ausdehnung von K4LiH3(SO4)4 weisen darauf hin, daß anomale Änderungen der spontanen Polarisation, die bei pyroelektrischen Untersuchungen in der Umgebung von 114 K beobachtet werden, keine Konsequenzen von strukturellen Änderungen der Parameter des Kristallgitters zu sein scheinen.