Ce-doped YAG and LuAG Epitaxial Films for Scintillation Detectors

Abstract

Epitaxial garnet films of undoped and Ce <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3+</sup> -doped yttrium aluminum garnet (YAG) and lutetium aluminum garnet (LuAG) were grown by the isothermal liquid phase epitaxy from two different fluxes: we used a standard PbO-B <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> flux and, as a novelty, BaO-B <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> -BaF <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> flux. It is shown that the films obtained from the lead-free BaO flux exhibited superior luminescent properties comparable with those of Czochralski grown single crystals. A detailed comparison of optical, luminescent, and kinetic properties of films grown from these two types of fluxes is made.