Ultrafast chemical dynamic behavior in highly epitaxial LaBaCo<sub>2</sub>O<sub>5+δ</sub> thin films
16
Citations
31
References
2014
Year
Electrical ResistanceElectrical EngineeringVarious TemperaturesEngineeringRedox ReactionsPhysicsMaterial AnalysisOxidation ResistanceSurface ScienceApplied PhysicsCondensed Matter PhysicsRedox ChemistryThin Film Process TechnologyThin FilmsEpitaxial GrowthThin Film ProcessingElectrochemistry
The redox reactions of highly epitaxial LaBaCo<sub>2</sub>O<sub>5+δ</sub> (LBCO) thin films exposed to the switching flow of reducing (H<sub>2</sub>) and oxidizing (O<sub>2</sub>) gases were examined at various temperatures between 260 and 700 °C. Their electrical resistance was measured using a precise ac bridge measurement system.