Pseudohalide‐Induced Moisture Tolerance in Perovskite CH₃NH₃Pb(SCN)₂I Thin Films

Abstract

Two pseudohalide thiocyanate ions (SCN(-) ) have been used to replace two iodides in CH3 NH3 PbI3 , and the resulting perovskite material was used as the active material in solar cells. In accelerated stability tests, the CH3 NH3 Pb(SCN)2 I perovskite films were shown to be superior to the conventional CH3 NH3 PbI3 films as no significant degradation was observed after the film had been exposed to air with a relative humidity of 95 % for over four hours, whereas CH3 NH3 PbI3 films degraded in less than 1.5 hours. Solar cells based on CH3 NH3 Pb(SCN)2 I thin films exhibited an efficiency of 8.3 %, which is comparable to that of CH3 NH3 PbI3 based cells fabricated in the same way.