Diffusion of platinum in the FePt system

Abstract

The homodiffusion coefficients D of platinum in Fe–Pt solid solutions in the concentration interval 15 to 60 at% Pt and in the temperature range 780 to 1420°C are determined by the residual activity method using the isotope Pt-193m. The measured residual activity values are evaluated by the spline-polynomial technique on a ZPA 600 computer. All the D-values satisfy the Arrhenius relation making possible the calculation of the migration characteristics D0 and δH. The results are discussed on the basis of the Fe–Pt equilibrium diagram. The increase of activation enthalpy δ(δH) due to the FePt ordered structure is 6.8 kcal/mol, i.e. about 11% of the value obtained by a linear interpolation and expected in a regular solid solution. Die Homodiffusionskoeffizienten D von Platin in Fe–Pt-Mischkristallen werden im Konzentrationsbereich 15 bis 60 At% Pt und im Temperaturintervall 780 bis 1420°C durch die Restaktivitätsmethode mit dem Isotop Pt-193m bestimmt. Die gemessenen Werte der Restaktivität werden mit der Spline-Polynomtechnik auf einem ZPA 600-Computer berechnet. Alle D-Werte erfüllen die Arrheniusbeziehung und machen eine Berechnung der Wanderungsgrößen D0 und δH möglich. Die Ergebnisse werden auf der Grundlage des Fe–Pt-Gleichgewichtsdiagramms diskutiert. Der Anstieg der Aktivierungsenthalpie δ(δH) infolge der geordneten FePt-Struktur beträgt 6,8 kcal/Mol, das sind etwa 11% des durch lineare Interpolation erhaltenen und für eine reguläre Festkörperlösung erwarteten Wertes.