Journal of the American Ceramic Society · 2005 · 16 citations · 4 references
Natural SciencesMaterials EngineeringMaterials ScienceMaterials ChemistryMaterials ProcessingNanomaterialsCatalytic MaterialsChemical ReductionMechanochemistryMetal Oxide NanomaterialsNanoparticle SynthesisPowder ProcessingCarbothermal ReductionChemical Reduction SynthesisDirect SynthesisMetal Oxide Nanoparticle SynthesisMetal Oxide Nanoparticles SynthesisMillingMilling ProcessesNanoparticle Formation
Carbothermic reduction of natural wolframite (FeWO 4 ) to nano‐sized tungsten carbide (WC) particles was achieved by calcining mechanically activated mixtures of FeWO 4 and active carbon at 1100°C under flowing Ar gas. The average particle size ranged between 20 and 25 nm. Intermediates, Fe 6 W 6 C and Fe 3 W 3 C, were observed between 900° and 1100°C, which decomposed to give the final product, WC. Homogeneity increase and associated decrease in the diffusion path by milling are mainly responsible for the successful production of WC. The process paves the way to rational utilization of natural FeWO 4 directly to fine advanced materials.
4