Investigations of the Thermoelectric Power at High Hydrogen Pressure in the NiH and PdH Systems

Abstract

The thermoelectric powers of NiH and PdH systems have been investigated at high hydrogen pressures (up to 14000 at) at 303 °K. It was found that in the case of the NiH system, the β-phase formed at about 7000 at has an nearly stoichiometric composition (H/Ni = 0.97). The nearly linear dependence of the absolute thermoelectric power of the NiH system on the atomic ratio can be explained in terms of a two-phase structure of the sample in a wide range of composition. In the pure β-phase the PdH system shows a linear dependence of the absolute thermoelectric power on the logarithm of the hydrogen fugacity. Die Thermokräfte von NiH- und PdH-Systemen wurden unter hohen Wasserstoffdrücken (bis 14000 at) bei einer Temperatur von 303 °K bestimmt. Im Falle des NiH-Systems wurde gefunden, daß die bei etwa 7000 at gebildete β-Phase eine nahezu stöchio-metrische Zusammensetzung aufweist (H/Ni = 0,97). Die etwa lineare Abhängigkeit der absoluten Thermokraft des NiH-Systems von dem Atomverhältnis H/Ni kann durch das Vorliegen zweier Phasen in der Probe innerhalb eines breiten Konzentrationsbereiches erklärt werden. Das PdH-System weist in der reinen β-Phase eine lineare Abhängigkeit der absoluten Thermokraft vom Logarithmus der Wasserstoffflüchtigkeit auf.