Effect of the rutile content on the photovoltaic performance of the dye-sensitized solar cells composed of mixed-phase TiO₂photoelectrodes

Abstract

The effect of the rutile content on the photovoltaic performance of dye-sensitized solar cells (DSSCs) composed of mixed-phase TiO(2) photoelectrode has been investigated. The mixed-phase TiO(2) particles with varied amounts of rutile, relative to anatase phase, are synthesized by an in situ method where the concentration of sulfate ion is used as a phase-controlling parameter in the formation of TiO(2) using TiCl(4) hydrolysis. The surface area (S(BET)) varies from 33 (pure rutile) to 165 (pure anatase) m(2) g(-1). Generally, both the current density (J(sc)) and photo-conversion efficiency (η) decrease as the rutile content increases. The incorporation of rod-shaped rutile particles causes low uptake of dye due to the reduced surface area, as well as slow electron transport in less efficiently-stacked structure. However, maximum J(sc) (14.63 mA cm(-2)) and η (8.69%) appear when relatively low rutile content (16%) is employed. The reported synergistic effect by the efficient interparticle electron transport from rutile to anatase seems to overbalance the decrease of surface area when small amount of rutile particles is incorporated.