Thermal and dynamic mechanical properties of organic–inorganic hybrid composites of itaconate‐containing poly(butylene succinate) and methacrylate‐substituted polysilsesquioxane

Abstract

Abstract Itaconate‐unit‐containing poly(butylene succinate) (PBSI) was synthesized by the reaction of 1,4‐butanediol, succinic acid, and itaconic acid in a molar ratio of 2.0 : 1.0 : 1.0, and the obtained PBSI was reacted with methacryl‐group‐substituted polysilsesquioxane (ME‐PSQ) in the presence of benzoyl peroxide (BPO) at 130°C to produce PBSI/ME‐PSQ hybrid composites. The thermal and dynamic mechanical properties of the PBSI/ME‐PSQ hybrid composites were investigated in comparison with those of PBSI cured at 130°C in the presence of BPO. As a result, the hybrid composites showed a much higher thermal degradation temperature and storage modulus in the rubbery state than the cured PBSI (C‐PBSI). The thermal degradation temperature and storage modulus of the hybrid composites increased with increasing ME‐PSQ content. The glass‐transition temperature, measured by dynamic mechanical analysis of the hybrid composites, somewhat increased with increasing ME‐PSQ content. However, the glass‐transition temperatures of all the hybrid composites were lower than that of C‐PBSI. Although the IR absorption peak related to CC groups was not detected for C‐PBSI, some olefinic absorption peaks remained for all the hybrid composites. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008