Adhesion Improvement of Poly(Phenylene-Vinylene) Substrates Induced by Argon-Oxygen Plasma Treatment

Abstract

Abstract Copper films evaporated on argon-oxygen plasma-treated poly(phenylene-vinylene) films have been studied by scratch test, X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM). The adhesion of the metallic film to the polymer substrate was greatly enhanced after treatment and found to increase with the treatment time. SEM observation of the treated samples revealed that the morphology of the polymer surface was gradually changed with the treatment time as compared with that of the bare polymer film. On the other hand, XPS analysis of the polymer-metal interface showed that the bonding between carbon, oxygen and copper were subsequently modified as compared with those obtained in untreated samples. The high adhesion strength observed on these substrates was related to the modification in the surface morphology on the one hand and to the formation of new compounds at the polymer-metal interface on the other. The nature of the interfacial layer and its influence on the adhesion of the copper layer was discussed by comparing the results with those obtained in poly(phenylene-vinylene) (PPV)-Al systems.