Preparation and magnetic study of the CoFe<sub>2</sub>O<sub>4</sub>-CoFe<sub>2</sub> nanocomposite powders

Abstract

Ferri-ferromagnetic nanocomposites CoFe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">4</sub> -CoFe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> were prepared via reduction of the cobalt ferrite CoFe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">4</sub> into a hydrogen atmosphere and by heat treatments. This preparation method yielded powders with relative volume fraction of CoFe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">4</sub> and CoFe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> in the range 0-0.91. The structure and the room temperature magnetization of the samples were analyzed by X-ray diffraction, scanning electron microscope (SEM) and transmission electron microscope (TEM), and by vibrating sample magnetometry, respectively. It was found that the saturation magnetization of the nanocomposite powders increases with the volume fraction of the ferromagnetic phase while their coercivity decreases. The highest value (5 kJ/m <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sup> ) for the maximum energy product (BH) <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">max</sub> was obtained for the sample containing 91% in volume of CoFe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> . This (BH) <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">max</sub> is 19% higher than the value measured in pure CoFe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">4</sub> . The magnetic field dependence of the magnetization did also behave as the nanocomposite powders were single-phase materials. This result indicates that the hard ferrimagnet CoFe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">4</sub> and the soft ferromagnet CoFe <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> are effectively exchange coupled and that their magnetization reverses cooperatively in the range of compositions investigated.