Spatial replica of ferromagnetic domains in iron-silicon alloys

Abstract

The decomposition of some iron-silicon alloys at low temperatures is influenced by spontaneous magnetization in each ferromagnetic domain. The anisotropic decomposition structure is frozen in by cooling and in this way a spatial replica of magnetic domain structure is produced, which was present in the sample at the time of ageing (at a temperature of about 600 °C). It is then revealed at room temperature on any cut through a bulk specimen. All 90 and 180° domain walls are clearly visible. Spatial reconstruction of the internal magnetic domain structure was performed by successive polishing and etching. By the same method the interaction of domain walls with dislocation networks was observed. Die Gefügeumwandlung von einigen Eisen-Silizium-Legierungen bei Temperaturen im Bereich von 600 °C wird durch die spontane Magnetisierung in jedem ferromagnetischen Bereich beeinflußt. Die anisotrope Umwandlungsstruktur wird durch Abkühlung eingefroren. Es entsteht dadurch ein räumlicher Abdruck der in der Probe während des Glühens existierenden, magnetischen Bereichsstruktur. Der Abdruck kann in jedem Querschnitt der massiven Probe sichtbar gemacht werden. Alle 180- und 90°-Wände sind deutlich zu unter-scheiden. Der räumliche Aufbau der inneren Bereichstruktur konnte dadurch rekonstruiert werden, daß die Probe stufenweise poliert und geätzt wurde. Mit derselben Methode wurde die Wechselwirkung der Blochwände mit dem Versetzungsnetzwerk beobachtet.