Large magnetic field-induced work output in a NiMnGa seven-layered modulated martensite

Abstract

We report the performance of a Ni-Mn-Ga single crystal with a seven-layered lattice modulation (14M martensite), demonstrating large actuation work output driven by an external magnetic field. A magnetic field-induced strain of 11.2%, a twinning stress of 0.64 MPa, and a magneto-crystalline anisotropy energy of 195 kJ/m3 are measured at room temperature, which exceed the best results reported in Ni-Mn-Ga 14M martensites. The produced magnetically induced work output of about 70 kJ/m3 makes the material attractive for actuator applications. Detailed XRD investigation reveals that the studied 14M martensite is stress-induced. With increasing compression stress, the stress-induced intermartensitic transformation sequence 10M → 14M → NM was demonstrated.