Internal friction peaks due to dislocation relaxations in plastically deformed and/or irradiated high-purity α-iron. II. Interpretation

Abstract

Interpretations of the internal friction peaks α, β1, β2, and γ observed (Part I) in plastically deformed and/or low-temperature neutron-irradiated α-iron are presented. The main component of the-peak α is attributed to the generation of kink pairs on non-screw dislocations, while the γ peak is ascribed to the analogous phenomenon on screw dislocations. β1 is identified with the thermally assisted unpinning of string-like, non-screw dislocations from immobile point defects. A second point-defect-dislocation interaction peak, β2, is ascribed to the dragging of the interstitial-type defects which become mobile at about 230 K by geometrical kinks on screw dislocations. A component α′ of the composite α peak is attributed to the trapping and detrapping of geometrical kinks on non-screw dislocations at immobile point defects. Cet article présente l'interprétation des pics de frottement intérieur α, β1, β2 et γ observés (Partie I) dans le fer alpha deformé plastiquement et/ou irradié aux neutrons à basse température. La principale composante du pic α est attribuée à la formation de double décrochements sur les dislocations non vis, et le pic γ correspond au měme phénomène sur les dislocations vis. β1 correspond à l'épinglage-désépinglage thermique des dislocations non vis, traitées comme des cordes vibrantes, sur des défauts immobiles. Le second pic d'interaction β2, s'explique par un drainage des défauts de type interstitiel, devenus mobiles vers 230 K, par les décrochements géométriques des dislocations vis. La seconde composante α′ du pic α est attribuée au piégage-dépiéegage des décrochements géométriques des dislocations non vis sur des défauts ponctuels immobiles.