High-potential magnetic anisotropy of CoPtCr-SiO/sub 2/ perpendicular recording media

Abstract

The magnetic anisotropy of CoPtCr-SiO/sub 2/ perpendicular recording media, including higher energy terms, was studied as a function of film composition and seed layer materials. All series of CoPtCr films with various Cr content, deposited on Ru seed layers, show maximum values of total anisotropy K/sub u/ at 25-30 at%Pt. The maximum value for CoPt(Cr=0) films reaches /spl sim/15/spl times/10/sup 6/ erg/cm/sup 3/. The addition of SiO/sub 2/ to the CoPtCr films reduces the grain K/sub u/, however the grain K/sub u/ maintains a large value of 8/spl times/10/sup 6/ erg/cm/sup 3/ even when 10at%SiO/sub 2/ is added to (Co/sub 90/Cr/sub 10/)/sub 80/Pt/sub 20/, for instance, which indicates the high-potential thermal stability. Theoretical calculations for media designs of 400 Gbits/in/sup 2/ revealed that the ratio of the high-energy anisotropy term K/sub u2/ to K/sub u1/(K/sub u/=K/sub u1/+K/sub u2/) is required to be 0.2-0.35 to enhance the energy barrier for the remanent state, without a notable change in switching field. The films deposited on Ru seed layers were found to show negligibly small K/sub u2/ values, however, the values of K/sub u1/ and K/sub u2/ vary significantly with the seed layer material used. K/sub u1/ decreases almost linearly as the K/sub u2/ value increases. It is concluded that CoPtCr films have a sufficient potential in the values of K/sub u1/ and K/sub u2/ for high-density perpendicular media.