Fracture and Fatigue Tolerant Steel Pressure Vessels for Gaseous Hydrogen

Abstract

Fatigue crack growth rates and rising displacement fracture thresholds have been measured for a 4130X steel in 45 MPa hydrogen gas. The ratio of minimum to maximum load (R-ratio) and cyclic frequency was varied to assess the effects of these variables on fatigue crack growth rates. Decreasing frequency and increasing R were both found to increase crack growth rate, however, these variables are not independent of each other. Changing frequency from 0.1 Hz to 1 Hz reduced crack growth rates at R = 0.5, but had no effect at R = 0.1. When applied to a design life calculation for a steel pressure vessel consistent with a typical hydrogen trailer tube, the measured fatigue and fracture data predicted a re-inspection interval of nearly 29 years, consistent with the excellent service history of such vessels which have been in use for many years.