Microstructural evolution and wear characteristics of equal channel angular pressing processed semi-solid-cast hypoeutectic aluminum alloys

Abstract

This work investigated the microstructural evolution of Al–7Si–Mg alloy cast semi-solid using a cooling slope as well as conventional casting followed by equal channel angular pressing (ECAP) in a 120° die. Feed materials were prepared for ECAP by cooling slope casting and by conventional casting. The microstructure of the processed alloys extruded was observed by optical microscope and by transmission electron microscope, and their hardness and wear resistance were evaluated. After ECAP processing, the primary α-Al phase tended to be elongated while the Si particles became fragmented and more nearly globular in shape and uniform in size than in the as-cast sample. The microstructure of the cooling slope-cast ECAPed samples was more homogenous than that of the conventionally cast ECAPed sample. The α-Al phase sub-grains were refined to sub-micrometer sizes for samples cast by both methods after ECAP. The hardness of the cooling slope-cast ECAPed sample was also higher than that of the conventionally cast ECAPed sample. The wear resistance of the alloy improved after cooling slope casting and ECAP processing.