Easy-glide hardening of Zn and Cd between 4.2 and 400 K

Abstract

The work hardening coefficient in the easy glide range is measured on Zn and Cd single crystals in the temperature range from 4.2 to 400 K. For low temperatures T/Tm ⪅ 0.15 work hardening was found to decrease rapidly with rising temperature, passes a minimum and at T/Tm = 0.3 there is a well developed maximum of work hardening. The location of this maximum depends on the shear strain rate. If the temperature becomes T/Tm ⪆ 0.3 the well known decrease of work hardening due to recovery processes can be observed. The measured temperature dependence of work hardening is contradictory to the established theories of work hardening of hexagonal metals, which affirm a constant ∂A in the low temperature range. Der Verfestigungskoeffizient des Bereiches A von Zn- und Cd-Einkristallen wurde erstmals im ganzen Temperaturbereich von 4,2 bis 400 K durchgehend gemessen. Die Verfestigung nimmt im Tieftemperaturbereich T/Tm ⪅ 0,15 für steigende Temperaturen stark ab, durchläuft ein Minimum und zeigt bei T/Tm = 0,3 ein deutliches Maximum, dessen Lage von der Verformungsgeschwindigkeit abhängt. Für T/Tm ⪆ 0.3 wird die bekannte Abnahme der Verfestigung auf Grund von Erholungsprozessen beobachtet. Die Temperatur-abhängigkeit ∂A(T) steht im Widerspruch zu den gängigen Verfestigungstheorien, die einen Konstanzbereich für T/Tm > 0,3 vorhersagen.