Influence of Light-polymerization Modes on the Degree of Conversion and Mechanical Properties of Resin Composites: A Comparative Analysis Between a Hybrid and a Nanofilled Composite

Abstract

This study analyzed the influence of the light polymerization mode on the degree of conversion (DC) and mechanical properties of two resin composites: a hybrid (Filtek P60) and a nanofilled composite (Filtek Supreme). The composites were light activated by three light polymerization modes (Standard-S: 650 mW/cm2 for 30 seconds; High intensity-H: 1000 mW/cm2 for 20 seconds and Gradual-G: 100 up to 1000 mW/cm2 for 10 seconds + 1000 mW/cm2 for 10 seconds). The DC (%) was measured by FT-Raman spectroscopy. Flexural strength and flexural modulus were obtained from bar-shaped specimens (1 x 2 x 10 mm) submitted to the three-point bending test. Microhardness was evaluated by Knoop indentation (KHN). Data were analyzed by ANOVA and Student-Newman-Keuls multiple range test and linear regression analysis. The results showed the following DC: H > S > G (p < 0.0001) and hybrid > nanofilled (p < 0.005). Correlation was found between DC and the radiant exposure (R2 = 0.92). With respect to mechanical properties, only KHN was significantly influenced by the light polymerization mode, as follow: H > S = G (p < 0.0001). The hybrid composite presented higher flexural strength and flexural modulus than the nanofilled composite (p < 0.0001). No significant difference was found in KHN between thetwo composites (p = 0.1605). The results suggest that nanofilled composites may present a lower degree of conversion and reduced mechanical properties compared to hybrid composites.