Hydrothermal synthesis of copper selenides with controllable phases and morphologies from an ionic liquid precursor

Abstract

Cu2−xSe nanocrystals and CuSe nanoflakes are successfully synthesized through a convenient hydrothermal method from an ionic liquid precursor 1-n-butyl-3-ethylimidazolium methylselenite ([BMIm][SeO2(OCH3)]). The phases and morphologies of the copper selenides can be controlled by simply changing the atom ratio of Cu/Se in the reactants and reaction temperature. Furthermore, it is found that the [BMIm][SeO2(OCH3)] not only serves as Se source but also has influence on the shapes of CuSe nanoflakes. The adsorption of alkyl imidazolium rings ([BMIm]+) onto the (0001) facets of covellite CuSe prohibits the growth in the [0001] direction, and CuSe nuclei growth mainly processes along the six symmetric directions (±[011], ±[10], and ±[100]) to form flakelike CuSe. The obtained copper selenides are characterized by XRD, SEM, EDS, XPS, TEM, and HRTEM. The results indicate that the Cu2−xSe nanocrystals are nearly spherical particles with an average diameter of about 20 nm, the hexagonal CuSe nanoflakes are single crystals with an edge length of 100–400 nm and a thickness of 25–50 nm. The potential formation mechanism of the copper selenides is also proposed.