Stereospecific Polymerization of Dialkyl Muconates through Free Radical Polymerization:  Isotropic Polymerization and Topochemical Polymerization

Abstract

Radical polymerization of dialkyl muconates (dialkyl 2,4-hexadienoates) was investigated in an isotropic (amorphous) state, that is, solution or bulk polymerization, and in a crystalline state. In the bulk polymerization at 120 °C in the presence of a radical initiator, high molecular weight polymers of more than 10 5 were obtained in high yields, compared with those in solution polymerization. Three kinds of isomers, cis,cis-, cis,trans-, and trans,trans- muconates, showed similar polymerization reactivities. The microstructure in the polymers was determined by 1 H and 13 C NMR spectroscopies to be 84−91%, 6−13%, and 2−4% for trans- 1,4-, cis- 1,4-, and 1,2-structures, respectively, which depended on the polymerization temperature. In contrast with the bulk (in the melt) and solution polymerizations, we discovered that diethyl cis,cis- muconate underwent highly stereospecific polymerization in a crystalline state under UV irradiation via a topochemical polymerization mechanism. The resulting polymer was of ultrahigh molecular weight ([η]) = 10 3 cm 3 /g) with high stereoregularity and crystallinity. This polymer has been clarified to be a tritactic polymer, trans- 1,4- meso- diisotactic or trans- 1,4- meso- disyndiotactic polymer.