Investigation on interface of Al/Cu couples in compound casting

Abstract

The joining of Al and Cu commercially pure metals using the compound casting process has been investigated where an aluminium melt is cast onto a solid cylindrical copper insert. The microstructure of the interface between copper core and surrounding aluminium was characterised by optical microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy and Vickers hardness tests. Results showed that five separate reaction layers are formed in the reaction interface of core and surrounding Al. These layers included Cu 9 Al 4 , AlCu and Al 2 Cu intermetallic compounds; a eutectic layer; and a eutectic α-Al dendritic structure layer. Owing to the presence of hard and brittle intermetallic compounds within reaction layers, microhardness profile showed a peak of 300 HV where both parent metals have hardness <50 HV. Microhardness profile also showed that hardness decreases from the copper to the aluminium side.