Atmospheric corrosion of mild steel. Part I - Rural and urban atmospheres

Abstract

This paper summarizes the results obtained in the MICAT project for mild steel specimens exposed for 1 to 4 years in 22 rural and urban atmospheres in the Ibero-American region. Test site characterization and chemical and morphological determination of the steel corrosion product layers (SCPLs) contributed to understanding the corrosion phenomena involved. It was observed how some climatological factors could affect steel corrosion rates and SCPL properties. Although the studied atmospheres were classified into different ISO groups, steel corrosion rates did not differ significantly between them. The only common characteristic of these atmospheres was an increase in SCPLs protectiveness with exposure time. Atmosphärische Korrosion von unlegiertem Stahl. Teil I – Land- und Stadtatmosphäre Die Arbeit fasst die Ergebnisse zusammen, die in dem MICAT Projekt für unlegierte Stahlproben, die 1 bis 4 Jahre in 22 ländlichen und städtischen Atmosphären in der Ibero-Amerikanischen Region ausgelagert waren, erhalten wurden. Die Charakterisierung der Versuchsstandorte und die chemische und morphologische Bestimmung der Stahlkorrosionsproduktschichten tragen zum Verständnis der beteiligten Korrosionsphänomene bei. Es wurde beobachtet, wie einige klimatologische Faktoren die Korrosionsgeschwindigkeiten und die Eigenschaften der Korrosionsproduktschicht beeinflussen können. Obwohl die untersuchten Atmosphären in verschiedene ISO Gruppen klassifiziert waren, unterschieden sich die Stahlkorrosionsgeschwindigkeiten nicht nennenswert voneinander. Das einzige gemeinsame Merkmal dieser Atmosphären war eine Zunahme der Schutzeigenschaften der Korrosionsproduktschichten mit der Auslagerungszeit.