Modification of critical current density of MgB2 films irradiated with 200 MeV Ag ions

Abstract

The effect of 200 MeV Ag ion irradiation on the temperature and field dependence of critical current density (JC) of high quality MgB2 thin films is studied. Substantial increase in JC is observed over a certain field range for the film irradiated at a dose of 1012 ions/cm2. Our analysis suggests that columnar defects are not formed under irradiation conditions used in these studies, which correspond to an electronic energy loss of about 16 keV/nm. Defects clusters are likely to be responsible for the observed improvement in JC.