High-Pressure Investigation of Li₂MnSiO₄ and Li₂CoSiO₄ Electrode Materials for Lithium-Ion Batteries

Abstract

In this work, the high-pressure behavior of Pmn2(1)-Li(2)MnSiO(4) and Pbn2(1)-Li(2)CoSiO(4) is followed by in situ X-ray diffraction at room temperature. Bulk moduli are 81 and 95 GPa for Pmn2(1)-Li(2)MnSiO(4) and Pbn2(1)-Li(2)CoSiO(4), respectively. Regardless of the moderate values of the bulk moduli, there is no evidence of any phase transformation up to a pressure of 15 GPa. Pmn2(1)-Li(2)MnSiO(4) shows an unusual expansion of the a lattice parameter upon compression. A density functional theory investigation yields lattice parameter variations and bulk moduli in good agreement with experiments. The calculated data indicate that expansion of the a lattice parameter is inherent to the crystal structure and independent of the nature of the transition-metal atom (M). The absence of pressure-driven phase transformation is likely associated with the incapability of the Li(2)MSiO(4) composition to adopt denser structures while avoiding large electrostatic repulsions.