Compatibilization of PP/EPDM blends by grafting acrylic acid to polypropylene and epoxidizing the diene in EPDM

Abstract

Abstract In this article, ethylene–propylene–diene‐rubber (EPDM) was epoxidized with an in situ formed performic acid to prepare epoxided EPDM (eEPDM). The eEPDM together with the introduction of PP‐ g ‐AA was used to compatibilize PP/EPDM blends in a Haake mixer. FTIR results showed that the EPDM had been epoxidized. The reaction between epoxy groups in the eEPDM and carboxylic acid groups in PP‐ g ‐AA had taken place, and PP‐ g ‐EPDM copolymers were formed in situ . Torque test results showed that the actual temperature and torque values for the compatibilized blends were higher than that of the uncompatibilized blends. Scanning electron microscopy (SEM) observation showed that the dispersed phase domain size of compatibilized blends and the uncompatibilized blends were 0.5 and 1.5 μm, respectively. The eEPDM together with the introduction of PP‐ g ‐AA could compatibilize PP/EPDM blends effectively. Notched Izod impact tests showed that the formation of PP‐ g ‐EPDM copolymer improved the impact strength and yielded a tougher PP blend. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3949–3954, 2006