MgB₂bulk and tapes prepared by mechanical alloying: influence of the boron precursor powder

Abstract

The influence of the quality of boron precursor powder on the microstructure and superconducting properties of MgB2 bulk samples and tapes was investigated. The nominal purity specified by the suppliers considers only metallic impurities and is not sufficient for the characterization of the boron precursor powder. Oxygen impurities and the grain size of the B precursor powder were found to affect Tc and the microstructure of the MgB2 tapes. The microstructure was investigated by SEM and TEM. Grains in the boron precursor powders were either nanocrystalline or crystalline, with grain sizes varying between 110 and 500 nm. MgB2 precursor powder was prepared by mechanical alloying, which resulted in a small, 20–60 nm, MgB2 grain size of bulk samples. Bulk samples showed the highest MgB2 phase fraction and a critical current density of 4.7 × 104 A cm−2 (at 20 K, 1 T) if boron precursor powder with small grain size and small fraction of metallic impurities was used. Such powder also yielded compact tapes and required lower annealing temperatures for the MgB2 phase formation. The typical critical current densities of the tapes were 5.0 × 104 A cm−2 (at 20 K, 3 T) and were significantly better than those of samples reported recently. These results underline the importance of mechanical alloying for enhancing the critical current density of MgB2 tapes. Summarizing, the phase content, the density and the superconducting properties of MgB2 bulk and tapes depend on the choice of boron precursor powder.