Dielectric properties of the KClKBr mixed crystal system

Abstract

Systematic measurements of the dielectric properties of mixed KClKBr crystal system are carried out in the frequency range 100 Hz to 100 kHz at room temperature to obtain composition variation of static dielectric constant (ε) and loss (tan δ). The temperature variation is measured in the same frequency range at temperatures ranging from room temperature to 320°C. This is the first report on detailed measurement of dielectric properties of KClKBr mixed crystals at room temperature as well as at elevated temperatures. The data are used to evaluate effective ionic charge, conductivity, and activation energy for conduction. All these properties are found to show a non-linear composition dependence. The temperature variation of dielectric constant for KCl, KBr, and the mixed crystals is analysed to obtain the anharmonic contribution to dielectric constant and effective ionic charge. Systematische Messungen der dielektrischen Eigenschaften von KClKBr-Mischkristallsystemen werden im Frequenzbereich 100 Hz bis 100 kHz bei Zimmertemperatur durchgeführt, um die Zusammensetzungsänderung der statischen Dielektrizitätskonstante (ε) und des Verlustfaktors (tan δ) zu erhalten. Die Temperaturänderungen werden im gleichen Frequenzbereich bei Temperaturen zwischen Zimmertemperatur und 320°C gemessen. Dies ist der erste Bericht ausführlicher Messungen der dielektrischen Eigenschaften von KClKBr-Mischkristallen sowohl bei Zimmertemperatur als auch bei erhöhgten Temperaturen. Diese Werte werden benutzt, um die effektive Ionenladung, die Leitfähigkeit und die Aktivierungsenergie für die Leitfähigkeit zu berechnen. Für alle diese Eigenschaften wird eine nichtlineare Abhängigkeit von der Zusammensetzung gefunden. Die Temperaturänderung der Dielektrizitätskonstante für KCl, KBr und Mischkristalle wird analysiert, um den anharmonischen Anteil zur Dielektrizitätskonstante und die effektive Ionenladung zu erhalten.