Shape- and size-controlled synthesis of nanometre ZnO from a simple solution route at room temperature

Abstract

Single crystalline ZnO nanorods with a diameter of about 5 nm were synthesized without the presence of any surfactants in ethanol solvent at room temperature. Nanodots and nanorods with different size and shape could be observed by TEM via simply altering NaOH concentration and reaction time. The polar ZnO nanorod growth mechanism was discussed by the 'Ostwald ripening' mechanism. Optical absorption and photoluminescence properties of ZnO nanorods have been characterized. The UV absorption spectrum revealed a clear blue-shift with a single absorption peak centred at 350 nm.