Dislocation generation from grain boundaries in nickel

Abstract

Experiments were conducted to determine the role played by grain boundaries in the premacroyield (ε = 3 × 10−4) deformation behaviour of pure nickel specimens possessing varying grain boundary structures. Examination in the transmission electron microscope of both annealed and deformed specimens showed many large bands of overlapping stacking faults and perfect dislocations which appeared to be produced from the thin foil edges due to foil handling. However, many examples of boundary emission of both partial and perfect dislocations were observed in some deformed specimens. This generation was found to be critically dependent on the grain boundary structure and was less significant at higher strains (ε = 1.5 × 10−2). The observed configurations were in qualitative agreement with several suggested models of grain boundary dislocation generation and provide some insight into yield initiation at grain boundaries. Es wurden Experimente durchgeführt, um die Rolle zu bestimmen, die Korngrenzen im „premacroyield”︁-Deformationsverhalten (ε = 3 ×−4) von reinen Nickelproben mit variierenden Korngrenzenstrukturen spielen. Eine Untersuchung im Transmissionselektronenmikroskop von getemperten und deformierten Proben zeigte viele große Banden von überlappenden Stapelfehlern und perfekten Versetzungen, die durch die Kanten der dünnen Foilen durch die Folienbearbeitung hervorgerufen zu werden scheinen. Jedoch wurden viele Beispiele von Grenzenemission von partiellen und perfekten Versetzungen in einigen deformierten Proben beobachtet. Es wurde gefunden, daß die Erzeugung kritisch von der Korngrenzenstruktur abhängt und bei höheren Dehnungen (ε = 1.5 × 10−2) weniger bedeutsam ist. Die beobachteten Konfigurationen befinden sich in qualitativer Übereinstimmung mit verschiedenen vorgeschlagenen Modellen der Korngrenzenerzeugung von Versetzungen und liefern einige Einsicht in die Flußauslösung an Korngrenzen.