Precipitates, zones and transitions during aging of Al-Zn-Mg-Zr 7000 series alloy

Abstract

Age hardening of an industrial 7000 series alloy in the temperature range 70-150° C has been followed by mechanical testing, electrical conductivity measurement, differential scanning calorimetry and extensive electron microscopy (TEM). The property changes during aging are interpreted in terms of structural transformations that involve two types of Guinier-Preston (GP) zones (I and II), the metastable hardening precipitate η′ and the stable phase η-MgZn2, as well as coarsening, changes of composition and internal order within zones and precipitates. Time-temperature ranges of the transformations during aging, and its dependence on quenching temperature, are estimated from TEM observations. The role of the GP(II) zones in the aging of alloys quenched from temperatures above 450°C is emphasized.