TEMPERATURE DEPENDENCE OF THE STRUCTURAL PARAMETERS IN THE TRANSFORMATION OF ARAGONITE TO CALCITE, AS DETERMINED FROM IN SITU SYNCHROTRON POWDER X-RAY-DIFFRACTION DATA

Abstract

The temperature dependency of the crystal structure and the polymorphic transition of CaCO{sub 3} from aragonite to calcite were studied using Rietveld structure refinement and high-temperature in situ synchrotron powder X-ray-diffraction data at ambient pressure, P. The orthorhombic metastable aragonite at room P, space group Pmcn, transforms to trigonal calcite, space group R{bar 3}c, at about T{sub c} = 468 C. This transformation occurs rapidly; it starts at about 420 C and is completed by 500 C, an 80 C interval that took about 10 minutes using a heating rate of 8 C/min. Structurally, from aragonite to calcite, the distribution of the Ca atom changes from approximately hexagonal to cubic close-packing. A 5.76% discontinuous increase in volume accompanies the reconstructive first-order transition. Besides the change in coordination of the Ca atom from nine to six from aragonite to calcite, the CO{sub 3} groups change by a 30{sup o} rotation across the transition.