Internal friction peaks due to dislocation relaxations in plastically deformed and/or irradiated high-purity α-iron

Abstract

The internal friction spectrum of deformed and/or neutron-irradiated high-purity iron is studied at a frequency of 0.5 Hz over the temperature range 4 to 470 K. It is found that the spectrum is very similar to those observed in other b.c.c. refractory metals. Thus, following the generally accepted classification of deformation peaks in b.c.c. metals, two peaks which originate from intrinsic dislocation relaxations are named α and γ; two other peaks arising from dislocation-point-defect interactions are called β1 and β2. This nomenclature is justified by a detailed interpretation of the experimental results, which is presented in a later paper (Part II). Le spectre de frottement interne du fer de haute pureté déformé et/ou irradié aux neutrons a été étudié à une fréquence de 0,5 Hz sur une gamme de température de 4 à 470 K. Le spectre obtenu s'apparente à ceux observés pour les autres métaux c.c. réfractaires. Ainsi, suivant la classification généralement acceptée pour les pics de frottement interne relatifs aux métaux c.c. déformés, deux pics provenant des relaxations intrinsèques de dislocation sont appelés α et γ, et deux autres provenant des interactions dislocations—défauts ponctuels β1 et β2. Cette nomenclature est justifiée dans une interprétation détaillée des résultats expérimentaux, qui sera présentée dans une deuxieme partie.