Helium desorption from a (110) Mo crystal. Evidence for the vacancy model in stage III annealing

Abstract

Helium desorption measurements with a Mo-crystal show (a) that during stage III annealing vacancies are removed but that (b) vacancies containing helium (HeV), which are immobile, are not affected. Since interstitials injected at room temperature do recombine with HeV's, it seems that, in stage III, vacancies become mobile and interstitials remain trapped (in e.g. clusters). These observations are supported by atomistic calculations. Measured desorption energies of helium from vacancies in Mo show good agreement with the calculated energies. Helium-Desorptionsmessungen an einem Mo-Kristall zeigen, daß während der Temperung des Zustands III (a) Leerstellen entfernt werden, daß jedoch (b) Leerstellen, die Helium (HeV) enthalten und die unbeweglich sind, nicht beeinflußt werden. DaZwischen-gitteratome, die bei Zimmertemperatur injiziert werden, mit den HeV rekombinieren, scheint es, daß im Zustand III die Leerstellen beweglich werden und die Zwischengitter-atome angehaftet bleiben (z. B. in Clustern). Diese Beobachtungen werden durch atomare Berechnungen unterstützt. Die gemessenen Desorptionsenergien von Helium aus Leerstellen in Mo zeigen gute Übereinstimmung mit den berechneten Energien.